关键词:
微观结构
两相
β-二氧化硅
强度
三氧化二铝
复合耐火材料
摘要:
Study on modules of rupture and microstructure of xphase bearing diphase β-Sialon and diphase β-Sialon/Al2O3 composites shows that MOR increases with tempera-ture rise up to a maximum oint and then decreases,For diphase β-Sialon materials,the maximum strength reaches 130 MPa-170 MPa at 1200℃;whereas for diphase β-Sialon/Al2O3 composites,the maximum strength reaches 200MPa-300 MPa at 1000℃,In the microstructure of th composite ,oblong crystals of x-phase and hexagonal prismatic crystals of β-Sialon are interlaced in the skeleton structure of *** struture creates a distinctly intensifying effect on the strength of the composite.